DESCRIPTION
BetonWood N cement bonded particle boards is the product that gives the company its name and is a material that adapts to multiple uses in the building industry. Made of high-density (1350 Kg/m³) Portland cement and stripped pine wood fibers, this particular panel guarantees an excellent solution for interventions aimed at obtaining high levels of thermal displacement, thanks to its high density which makes it suitable also for self-supporting dry screeds, radiant floors and stiffening structures.
BetonWood N panels combine the advantageous characteristics of concrete with the characteristics of wood. The structure of the panel is made of wood chips and fragments that form the upper layer on both sides, up to a rough layer in the central part. The surfaces of the edges are smooth, with a gray color, when the product does not undergo smoothing operations.
• insects and fungi are unable to attack or damage it;
• thanks to its physical and mechanical characteristics, the product is considered as one of the best lightweight construction materials;
• it is incombustible (A2 according to Standard DIN 4102);
• it is free from formaldehyde and free of asbestos, etc.;
• free of recycled Inks (present in materials with recycled cellulose);
• weather resistant;
• workable with wooden tools;
• high flow rate.
DIMENSIONS AND THICKNESSES AVAILABLE
| | Dimensions |
|---|
| Thickness |
1220 x 520 |
| 22 | • |
BetonWood N cement bonded particle boards are also available in Sanded version, coming from standard panels properly sanded and calibrated with special machines, to bring the thickness of the panels to lower dimensional tolerances. These particular panels have the characteristic of being aesthetically pleasing, since the wood contained inside stands out on the upper and lower part, compared to the standard panel, which instead has the particularity of having a totally cementitious appearance.
BetonWood cement bonded particle boards can be worked on the edges in order to facilitate the joints during laying:
• stepped edge for 22 mm thickness
• tongue & groove edges for 22 mm thickness
STORAGE / DELIVERY panels with sharp edges
| Dimension (mm) |
Thickness (mm) |
m³/panel |
kg/m² |
kg/panel |
Panels/pallet |
| 1220 x 520 |
22 |
0,013 |
30 |
18,8 |
56 |
STORAGE / DELIVERY panels with Tongue & Groove edges
| Dimension (mm) |
Thickness (mm) |
m³/panel |
kg/m² |
kg/panel |
Panels/pallet |
| 1220 x 520 |
22 |
0,013 |
30 |
18,8 |
56 |
STORAGE / DELIVERY panels Sanded with sharp edges
| Dimension (mm) |
Thickness (mm) |
m³/panel |
kg/m² |
kg/panel |
Panels/pallet |
| 1220 x 520 |
22 |
0,013 |
30 |
18,8 |
56 |
STORAGE / DELIVERY panels Sanded with Tongue & Groove edges
| Dimension (mm) |
Thickness (mm) |
m³/panel |
kg/m² |
kg/panel |
Panels/pallet |
| 1220 x 520 |
22 |
0,013 |
30 |
18,8 |
56 |
• the delivery of the material normally takes place by truck, considering the high mass of the pallets it is advisable that the recipient has suitable equipment and mechanical lifting equipment with minimum capacities of 35/40 quintals for unloading the goods;
• it is advisable to deposit the boards by stacking them one on top of the other and so as to keep them in a horizontal position, with supports having a square section and a minimum distance of 80 cm;
• individual panels must be transported by cutting, never horizontally;
• avoid direct exposure to sunlight and adequately cover the material to avoid excessive dust accumulation;
• the pallets are equipped with an upper protection plate, which must be repositioned each time over the other tables and weighted upward to avoid the distortion of the plates below it.
TECHNICAL CHARACTERISTICS
| Density (kg/m³) | 1350 |
| Fire resistance according to EN 13501-1 | A2-fl-s1 |
| Thermal conductivity coefficient λD W/(m∗K) | 0,26 |
| Specific heat [J/(kg∗K)] | 1880 |
| Resistance to vapor diffusion μ | 22,6 |
| Coefficient of linear thermal expansion α | 0,00001 |
| Thick swelling after 24 hours in water | 1,5% |
| Air permeability I/min. m² Mpa | 0,133 |
| Surface PH value | 11 |
| Flexural strength σ (N /mm²) | min.9 |
| Transverse tensile strength N (N /mm²) | min.0,5 |
| Cut resistance τ (N /mm²) | 0,5 |
| Elasticity module E (N /mm²) | 4500 |
| Resistance to distributed load kPa | 9000 |
| Resistance to concentrated load kN | 9 |
SOUNDPROOFING | Soundproofing power (dB)
| | Frequency (Hz) |
|---|
| Thickness | 100 | 200 | 400 | 800 | 1600 | 3150 |
|---|
| 18 | 17,5 | 22,6 | 27,8 | 33,2 | 38,7 | 44,0 |
|---|
| 20 | 18,3 | 23,5 | 28,7 | 34,1 | 39,6 | 45,0 |
|---|